Stanley 632“Extra Flow” weld metal for rapid repairs.
 |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
Nickel - iron "Non Conductive" electrode for joining dirty - contaminated cast irons and cast irons to steel.
• Flux coating does not side arc even after being heated.
• Extremely strong arc drive penetrates surface contaminants.
• Special slag composition can be welded over without creating porosity.
• Extra nickel content insures crack resistant machinable welds.
• Also available in TIG form as product code STANLEY 632 TIG. |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
TYPICAL MECHANICAL PROPERTIES :
Undiluted Weld Metal Maximum Value Up to:
Tensile Strength 70,000 Psi ( 500 MPa )
Yield Strength 49,000 Psi ( 350 MPa )
Elongation 20%
Hardness Rockwell B 88-90, Brinell 185,
Vickers 189
APPLICATIONS :
“Extra Flow” weld metal for rapid repairs.
Universal electrode for joining a wide variety of ductile, nodular and malleable cast irons.
Ideally suited for the repair of defective or cracked malleable iron castings.
RECOMMENDED CURRENT :
DC Reverse (+) or AC
WELDING POSITIONS :
Flat, Vertical up, Horizontal, Overhead.
WELDING TECHNIQUES :
Remove any surface contamination with the proper solvents. Adjust the welding machine to the lowest proper setting that yields good welding conditions. |
|