Silver Brazing, Brazing and Soldering |
|
 |
Stanley 60 FSuper active flux coated cadmium free silver brazing alloy with 56% silver content
 |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
Super active flux coated cadmium free silver brazing alloy with 56% silver content
- Rare flux coated silver available in 3/64" (1.2mm) diameter for precision work.
- Special "Fast Flow" flux coating provides twice the base metal cleansing action of conventional silver flux coatings.
- No odors from rubberized compounds yet the flux coating is totally flexible and non-fragile.
- The only flux coated silver flux strong enough to clean oxidized stainless steel.
|
|
Overview |
|
Specifications |
|
Email to a Friend |
|
APPLICATIONS:
For color matching stainless steel and for low temperature high
strength joints in the food, medical and pharmaceutical industries.
FLUX COLOR: Pink
TYPICAL MECHANICAL PROPERTIES:
Undiluted Weld Metal
Tensile strength
Yield strength
Elongation
Conductivity
Density
Hardness |
Maximum Value Up to:
71,000 PSI (490 N/mm2)
60,000 PSI (415 N/mm2)
25%
14.3
9.59/cm3
Brinell 130 |
TORCH SETTING: Slightly Carburizing
TEMPERATURE RANGES:
| Working Temperature: |
1210oF (655oC) |
| Melting Range: |
1140oF (620oC) Solidus
1200oF (650oC) Liquidus |
DEPOSITION RATES:
Diameter
(mm) |
Length
(mm) |
Weldmetal/
Rod |
Joint Length/1"
(25mm) of Rod |
| 3/64 (1.2) |
18" (450) |
.25oz (7.1g) |
17" (431mm) |
| 1/16 (1.6) |
18" (450) |
.33oz (9.2g) |
24" (600mm) |
| 3/32 (2.5) |
18" (450) |
.65oz (18g) |
44" (1100mm) |
WELDING TECHNIQUES:
After cleaning metal, preheat generally to 350oF (200oC) then heat the joint area to 800oF (420oC). Melt off some flux and allow it to flow throughout the joint. Then add alloy.
ELECTRODE PACKAGING & DIMENSIONS:
| Diameter(mm) |
3/64 (1.2) |
1/16 (1.6) |
3/32 (2.5) |
| Length (mm) |
18" (450) |
18" (450) |
18" (450) |
| Rods / lb |
55 |
32 |
16 |
| Rods/ kg |
121 |
70 |
35 |
| Feet/lb |
82.5 |
48 |
24 |
| Cm/kg |
5445 |
3150 |
1575 |
|
|
Overview |
|